COMPOSITIONin % BY MASS Co 64.0 · Cr 28.5 · Mo 5.0 · Si 1.0 · Mn 1.0 · C
ALLOY CHARACTERISTICSSTANDARD VALUES
Type (ISO 22674)5 Density8.3 g/cm 3 Preheating temperature950–1050 °C Solidus, liquidus temperature1265, 1395 °C Casting temperature approx.1460 °C Young’s modulus185 GPa Proof strength (Rp0.2)615 MPa Elongation after fracture (A5)10% Vickers hardness360 HV10